| Depending on the size, Speed and temperature of the users' wire rod process. HBW will supply HSS Rolling Rings that yield perfect steel products | |||||||||
◆◇ Unique Features
High V, W, Cr, Mo, Nb and other alloy elements. Carbide types: MC and M2C with high hardness and good abrasion resistance.
Excellet thermal stability, high hardness and good wear resistance.
High expansion coefficient and good thermal conductivity, more conducive to control.
Forming oxide film during rolling process, improving roll wear resistance significantly.
Super high strength of the roll core (DCI).
◆◇ Specification
KOCKS RING | |||
Brand | HBW ROLL | Material Code | HBWr03 |
Specification | Ø200-Ø550 | Each Re-machining | ≤0.8mm (reducing) |
Hardness | 60-63HRC | Surface Hardness Uniformity | ≤1.5HRC |
Features & Advantages | 1. High abrasion resistance | ||
2. Small hardness drop | |||
3. Less re-machining amount | |||
4. High wear resistance and impact toughness under thermal load | |||
5. No Bursting problem, especially when rolling large size bar above Ø20mm | |||
6. Good process ability with high machining efficiency | |||
| Application | KOCKS RSB. Applicable of special steel bar (finish size ≥Ø20mm ) rolling | ||
◆◇ Chemical Analysis
Material | HBW Patented Chemical Composition (%) | |||||||||||
C | Si | Mn | Cr | Ni | Mo | V | W | P & S | Nb | Co | Others | |
HSS (Alloy composition changes based on different grades) | 1.5 ~ 2.10 | 0.3 ~ 1.0 | 0.30 ~ 0.70 | 3.00 ~ 6.00 | 0.50 ~ 1.50 | 3.0 ~ 7.0 | 2.0 ~ 8.0 | 1.0 ~ 8.0 | ≤0.03 | Depends on HSS Grade | ||
◆◇ Physical Properties
| Properties | Tensile Strengt | Compressive Strength | |
| ≥700MPa | ≥2500MPa | ||
◆◇ Micro structure
Excellent Technical of HBW’s Patented Casting and HT Process Guarantee the Superior Micro-structure of each HSS Rolls.
Metallographic Micrograph are available to supply in HBW.
◆◇ Unique Features
High V, W, Cr, Mo, Nb and other alloy elements. Carbide types: MC and M2C with high hardness and good abrasion resistance.
Excellet thermal stability, high hardness and good wear resistance.
High expansion coefficient and good thermal conductivity, more conducive to control.
Forming oxide film during rolling process, improving roll wear resistance significantly.
Super high strength of the roll core (DCI).
◆◇ Specification
KOCKS RING | |||
Brand | HBW ROLL | Material Code | HBWr03 |
Specification | Ø200-Ø550 | Each Re-machining | ≤0.8mm (reducing) |
Hardness | 60-63HRC | Surface Hardness Uniformity | ≤1.5HRC |
Features & Advantages | 1. High abrasion resistance | ||
2. Small hardness drop | |||
3. Less re-machining amount | |||
4. High wear resistance and impact toughness under thermal load | |||
5. No Bursting problem, especially when rolling large size bar above Ø20mm | |||
6. Good process ability with high machining efficiency | |||
| Application | KOCKS RSB. Applicable of special steel bar (finish size ≥Ø20mm ) rolling | ||
◆◇ Chemical Analysis
Material | HBW Patented Chemical Composition (%) | |||||||||||
C | Si | Mn | Cr | Ni | Mo | V | W | P & S | Nb | Co | Others | |
HSS (Alloy composition changes based on different grades) | 1.5 ~ 2.10 | 0.3 ~ 1.0 | 0.30 ~ 0.70 | 3.00 ~ 6.00 | 0.50 ~ 1.50 | 3.0 ~ 7.0 | 2.0 ~ 8.0 | 1.0 ~ 8.0 | ≤0.03 | Depends on HSS Grade | ||
◆◇ Physical Properties
| Properties | Tensile Strengt | Compressive Strength | |
| ≥700MPa | ≥2500MPa | ||
◆◇ Micro structure
Excellent Technical of HBW’s Patented Casting and HT Process Guarantee the Superior Micro-structure of each HSS Rolls.
Metallographic Micrograph are available to supply in HBW.